ZC-5106
ZC-5106 Thermoplastic HFFR Compound
The material is used for thermoplastic low smoke halogen free flame retardant polyolefin sheath materials. It is produced through continuous mixing plasticizing granulation based on polyolefin as matrix, adding inorganic flame retardants, compatilizer, lubricants, antioxidant and other additives. The product has stable properties, good extrusion process ability, mechanical properties and flame retardant properties.
Application: flame retardant polyethylene wire and cable sheath layer; communication cable, control cable and power cable sheath; maximum working temperature is 90℃ .
Property
Item | Unit | Test method | Specification | Value | ||
Density@23℃ | g/cm3 | ASTM D792 | ≤1.55 | 1.49 | ||
Tensile Strength | MPa | IEC 60811- 1- 1 | ≥10.0 | 12.0 | ||
Elongation at Break | % | ≥125 | 170 | |||
Elongation at break@100℃ , 168h | Tensile Strength retention | % | IEC 60811- 1- 1 | ≥80 | 90 | |
Break Elongation retention | % | ≥80 | 85 | |||
Volume resistivity@20℃ | Ω• cm | IEC 60093 | ≥1.0×1013 | 1.0×1014 | ||
Dielectric strength@20C | MV/m | IEC60243- 1 | ≥18 | 28 | ||
Oxygen index | % | ISO 4589 | ≥30 | 32 | ||
Smoke density | Flaming | - | ASTM E662 | ≤100 | 75 | |
No Flaming | - | ≤350 | 270 | |||
Halogen acid gas content | mg/g | IEC 60745- 1 | ≤5 | 2 | ||
pH | - | IEC 60745- 1 | ≥4.3 | 6.0 | ||
Conductivity | us/mm | IEC 60745- 1 | ≤10 | 3 | ||
Remarks：
All values are given in good faith and based on our typical data but without warranty or guarantee expressed or implied.
ZC-5106 Thermoplastic HFFR Compound
The material is used for thermoplastic low smoke halogen free flame retardant polyolefin sheath materials. It is produced through continuous mixing plasticizing granulation based on polyolefin as matrix, adding inorganic flame retardants, compatilizer, lubricants, antioxidant and other additives. The product has stable properties, good extrusion process ability, mechanical properties and flame retardant properties.
Application: flame retardant polyethylene wire and cable sheath layer; communication cable, control cable and power cable sheath; maximum working temperature is 90℃ .
Property
Item | Unit | Test method | Specification | Value | ||
Density@23℃ | g/cm3 | ASTM D792 | ≤1.55 | 1.49 | ||
Tensile Strength | MPa | IEC 60811- 1- 1 | ≥10.0 | 12.0 | ||
Elongation at Break | % | ≥125 | 170 | |||
Elongation at break@100℃ , 168h | Tensile Strength retention | % | IEC 60811- 1- 1 | ≥80 | 90 | |
Break Elongation retention | % | ≥80 | 85 | |||
Volume resistivity@20℃ | Ω• cm | IEC 60093 | ≥1.0×1013 | 1.0×1014 | ||
Dielectric strength@20C | MV/m | IEC60243- 1 | ≥18 | 28 | ||
Oxygen index | % | ISO 4589 | ≥30 | 32 | ||
Smoke density | Flaming | - | ASTM E662 | ≤100 | 75 | |
No Flaming | - | ≤350 | 270 | |||
Halogen acid gas content | mg/g | IEC 60745- 1 | ≤5 | 2 | ||
pH | - | IEC 60745- 1 | ≥4.3 | 6.0 | ||
Conductivity | us/mm | IEC 60745- 1 | ≤10 | 3 | ||
Remarks：
All values are given in good faith and based on our typical data but without warranty or guarantee expressed or implied.