Silane XLPE Compound of Sioplas Method for Wire and Cable up to 3kV ZC-3201

5 0 Reviews
This material is a kind of warm water crosslinkable polyethylene insulation compound which consisted of compound A and compound B. Compound A is made from high quality polyethylene resin, imported silane coupling agent and compound B is made from organotin catalysts and antioxidant agent. Loss-in-weight Feeder which guarantees stable precision of components. It has an excellent extrusion performance and stable physical and chemical index; Quick extruding speed and smooth surface.
Availability:
Quantity:
facebook sharing button
twitter sharing button
line sharing button
wechat sharing button
linkedin sharing button
pinterest sharing button
whatsapp sharing button
sharethis sharing button
  • ZC-3201

ZC-3201    Silane XLPE Compound of Sioplas Method for Wire and Cable up to 3kV

This  material  is  a  kind  of  warm  water  crosslinkable  polyethylene  insulation  compound  which  consisted  of compound A  and compound  B.  Compound A  is  made from  high  quality  polyethylene  resin,  imported  silane coupling agent and compound B is made from organotin catalysts and antioxidant agent. Loss-in-weight Feeder which guarantees stable precision of components. It has an excellent extrusion performance and stable physical and chemical index; Quick extruding speed and smooth surface.

Application: Low voltage crosslinkable wire and cable insulation; Maximum working temperature is 90C. Property


Item

Unit

Test method

Standard

value

Typical

value

Tensile strength

MPa

IEC 60811- 1- 1

≥ 13.5

18.0

Elongation at break

%

≥350

470

Impact embrittlement performance@-76C

Failure number

Piece

ASTM D746

≤15/30

0/30

After aging

@135C, 168h

Tensile strength variation

%

IEC 60811- 1-2

± 20

+6

Breaking elongation variation

%

± 20

-3

Hot prolongation@200C, 0.2MPa, 15min

Elongation under the load

%

IEC 60811-2- 1

≤ 100

55

Permanent deformation

%

≤ 5

0

Dielectric dissipation factor@20C, 50HZ

IEC 60250

≤0.001

0.0001

Relative dielectric constant@20C, 50HZ

≤ 2.35

2.25

Dielectric strength@20C

MV/m

IEC 60243- 1

≥ 25

37

Volume resistivity@20C

Ω · m

IEC 60093

≥ 1 × 1014

6 × 1014

Gel content

%

ASTM D2765

≥ 60

66

Processing

Recommend to use polyethylene specific extruder. Draw ratio is from 18:1 to 25:1 and other equipment need to be adjusted according to the circumstance.


Zone

Feeding Section

Compression Section

Homogenization Section

Model Section

Temperature Range C

160- 180

180- 190

190-200

195-205

- Above temperature is only for reference.

Storage

Keep  at  room  temperature;  Storage  environment  should  be  clean,  dry  and  ventilated;  Best  use  within  six months from the date of production; Mix compound A and B, please use it up in 8 hours; Compound A should be used up within 24 hours after opened.

Product packing

- 25kg in each package, of which the grafted polyethylene (compound A) is 23.75kg/bag, catalytic masterbatch material (compound B) is 1.25 kg/bag;

- Compound A and B are in moisture resistant aluminum laminated bags with composite paper bags outside;

- Palletized bottom.


Previous: 
Next: 

ABOUT US

Our company is a professional company that engaged in production, sales, technology research, technology development and technical services of electrical system products, power engineering design and construction, electrical products, electrical equipment, sales, installation and technical services of energy storage equipment.

QUICK LINKS

PRODUCTS

CONTACT US

  2201-7&2201-8, Dongjiu Building, No.888 Jiefang East Road, Yixing City, Jiangsu Province
  +86-18020528228
  +86-510-87015096
   +86-18020528228/+86-18761555908
​Copyright © 2023 Jiangsu East Energy Electrical Engineering Co., Ltd.  苏ICP备16064163号-1 Technology by Leadong. Sitemap.

Related Products