ZC-4211
ZC-4211 Outer Strippable Semiconductive Shield Compound for MV Power Cable up to 35kV
This material is used for crosslinkeble semiconductive shielding material. It is produced by using high quality EVA resin, conductive black carbon as the main material, adding cross-linking agent, antioxidant and other additives; mixed granulation and fabrication process is stable and reliable in quality.
Application: Shielding material of 35kV crosslinkable polyethylene insulated cable insulation layer; Maximum working temperature is 90C.
Property
Item | Unit | Test method | Typical value | |
Density@23C | g/cm³ | ASTM D792 | 1.15 | |
Tensile strength | MPa | IEC60811- 1- 1 | 15.0 | |
Elongation at break | % | 320 | ||
Impact embrittlement performance@-40C | Failure number | Piece | ASTM D746 | 0/30 |
After aging @135C, 168h | Tensile strength variation | % | IEC 60811-1-2 | +8 |
Breaking elongation variation | % | -5 | ||
Hot prolongation@200C, 0.2MPa, 15min | Elongation under the load | % | IEC 60811-2- 1 | 60 |
Permanent deformation | % | 0 | ||
Volume resistivity@20C | Ω · cm | ASTM D257 | 45 | |
Volume resistivity@90C | Ω · cm | ASTM D257 | 220 | |
Peel strength | N/cm | ASTM D3330-02 | 38 |
Processing
Recommend to use specific extruder for shielding materials (draw ratio L/D = 20~25), other length to diameter ratio should be adjusted according to the circumstance. Recommend to use 60 to 80 type wire mesh filter.
Zone | 1 | 2 | 3 | 4 | 5 | Neck | Head | Die |
Temperature Range C | 65 | 85 | 95 | 105 | 105 | 105 | 105 | 105 |
- Above temperature is only for reference.
Storage
Keep at room temperature; Storage environment should be clean, dry and ventilated; Please dry it after a long-time opening.
Product packing
600kg in each package; Inner lined with plastic sealed film bag; Corrugated carton with tray at the bottom.
ZC-4211 Outer Strippable Semiconductive Shield Compound for MV Power Cable up to 35kV
This material is used for crosslinkeble semiconductive shielding material. It is produced by using high quality EVA resin, conductive black carbon as the main material, adding cross-linking agent, antioxidant and other additives; mixed granulation and fabrication process is stable and reliable in quality.
Application: Shielding material of 35kV crosslinkable polyethylene insulated cable insulation layer; Maximum working temperature is 90C.
Property
Item | Unit | Test method | Typical value | |
Density@23C | g/cm³ | ASTM D792 | 1.15 | |
Tensile strength | MPa | IEC60811- 1- 1 | 15.0 | |
Elongation at break | % | 320 | ||
Impact embrittlement performance@-40C | Failure number | Piece | ASTM D746 | 0/30 |
After aging @135C, 168h | Tensile strength variation | % | IEC 60811-1-2 | +8 |
Breaking elongation variation | % | -5 | ||
Hot prolongation@200C, 0.2MPa, 15min | Elongation under the load | % | IEC 60811-2- 1 | 60 |
Permanent deformation | % | 0 | ||
Volume resistivity@20C | Ω · cm | ASTM D257 | 45 | |
Volume resistivity@90C | Ω · cm | ASTM D257 | 220 | |
Peel strength | N/cm | ASTM D3330-02 | 38 |
Processing
Recommend to use specific extruder for shielding materials (draw ratio L/D = 20~25), other length to diameter ratio should be adjusted according to the circumstance. Recommend to use 60 to 80 type wire mesh filter.
Zone | 1 | 2 | 3 | 4 | 5 | Neck | Head | Die |
Temperature Range C | 65 | 85 | 95 | 105 | 105 | 105 | 105 | 105 |
- Above temperature is only for reference.
Storage
Keep at room temperature; Storage environment should be clean, dry and ventilated; Please dry it after a long-time opening.
Product packing
600kg in each package; Inner lined with plastic sealed film bag; Corrugated carton with tray at the bottom.