ZC-3211
ZC-3211 Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kV
This material is a kind of warm water crosslinkable polyethylene insulation compound which consisted of compound A and compound B. Compound A is made from high quality polyethylene resin, imported silane coupling agent and compound B is made from organotin catalysts and antioxidant agent. Loss-in-weight Feeder which guarantees stable precision of components. It has an excellent extrusion performance and stable physical and chemical index.
Application: 10kV and below aerial cable insulation; Maximum working temperature is 90℃.
Property
Item | Unit | Test method | Standard vaue | Typical value | |
Tensile strength | MPa | IEC 60811- 1- 1 | ≥ 13.5 | 18.5 | |
Elongation at break | % | ≥350 | 465 | ||
Impact embrittlement performance@-76℃ | Failure number | Piece | ASTM D746 | ≤ 15/30 | 0/30 |
After aging @135℃, 168h | Tensile strength variation | % | IEC 60811- 1-2 | ±20 | +7 |
Breaking elongation variation | % | ±20 | + 1 | ||
Hot prolongation@200℃, 0.2MPa, 15min | Elongation under the load | % | IEC 60811-2- 1 | ≤80 | 50 |
Permanent deformation | % | ≤5 | 0 | ||
Dielectric dissipation factor@20℃, 50HZ | － | IEC 60250 | ≤0.001 | 0.0003 | |
Relative dielectric constant@20℃, 50HZ | － | ≤ 2.35 | 2.25 | ||
Dielectric strength@20℃ | MV/m | IEC 60243- 1 | ≥25 | 37 | |
Volume resistivity@20℃ | Ω ·m | IEC 60093 | ≥ 5×1013 | 6×1014 | |
Environmental stress crack resistance F50 |
| IEC 811-4-1 | ≥ 1000 | Pass | |
Artificial climate aging resistance (after42 days ) | Tensile strength variation | % | GB/T 14049 | ±30 | - 19 |
Breaking elongation variation | % | ±30 | -25 | ||
Artificial climate aging resistance (after 21 days) | Tensile strength variation | % | ± 15 | -9 | |
Breaking elongation variation | % | ± 15 | - 11 | ||
Processing
Recommend for polyethylene specific extruder. Draw ratio is from 18:1 to 25:1 and other equipment need to be adjusted according to the circumstance.
Zone | Feeding Section | Compression Section | Homogenization Section | Model Section |
Temperature Range ℃ | 160- 180 | 180- 190 | 190-200 | 195-205 |
- Above temperature is only for reference.
Storage
Keep at room temperature; Storage environment should be clean, dry and ventilated; Best use within six months from the date of production; Mix compound A and B, please use it up in 8 hours; Compound A should be used up within 24 hours after opened.
Product packing
- 25kg in each package, of which the grafted polyethylene (compound A) is 23.75 kg/bag, catalytic master batch material (compound B) is 1.25 kg/bag.
- Compound A and B are in moisture resistant aluminum laminated bags with composite paper bags outside.
ZC-3211 Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kV
This material is a kind of warm water crosslinkable polyethylene insulation compound which consisted of compound A and compound B. Compound A is made from high quality polyethylene resin, imported silane coupling agent and compound B is made from organotin catalysts and antioxidant agent. Loss-in-weight Feeder which guarantees stable precision of components. It has an excellent extrusion performance and stable physical and chemical index.
Application: 10kV and below aerial cable insulation; Maximum working temperature is 90℃.
Property
Item | Unit | Test method | Standard vaue | Typical value | |
Tensile strength | MPa | IEC 60811- 1- 1 | ≥ 13.5 | 18.5 | |
Elongation at break | % | ≥350 | 465 | ||
Impact embrittlement performance@-76℃ | Failure number | Piece | ASTM D746 | ≤ 15/30 | 0/30 |
After aging @135℃, 168h | Tensile strength variation | % | IEC 60811- 1-2 | ±20 | +7 |
Breaking elongation variation | % | ±20 | + 1 | ||
Hot prolongation@200℃, 0.2MPa, 15min | Elongation under the load | % | IEC 60811-2- 1 | ≤80 | 50 |
Permanent deformation | % | ≤5 | 0 | ||
Dielectric dissipation factor@20℃, 50HZ | － | IEC 60250 | ≤0.001 | 0.0003 | |
Relative dielectric constant@20℃, 50HZ | － | ≤ 2.35 | 2.25 | ||
Dielectric strength@20℃ | MV/m | IEC 60243- 1 | ≥25 | 37 | |
Volume resistivity@20℃ | Ω ·m | IEC 60093 | ≥ 5×1013 | 6×1014 | |
Environmental stress crack resistance F50 |
| IEC 811-4-1 | ≥ 1000 | Pass | |
Artificial climate aging resistance (after42 days ) | Tensile strength variation | % | GB/T 14049 | ±30 | - 19 |
Breaking elongation variation | % | ±30 | -25 | ||
Artificial climate aging resistance (after 21 days) | Tensile strength variation | % | ± 15 | -9 | |
Breaking elongation variation | % | ± 15 | - 11 | ||
Processing
Recommend for polyethylene specific extruder. Draw ratio is from 18:1 to 25:1 and other equipment need to be adjusted according to the circumstance.
Zone | Feeding Section | Compression Section | Homogenization Section | Model Section |
Temperature Range ℃ | 160- 180 | 180- 190 | 190-200 | 195-205 |
- Above temperature is only for reference.
Storage
Keep at room temperature; Storage environment should be clean, dry and ventilated; Best use within six months from the date of production; Mix compound A and B, please use it up in 8 hours; Compound A should be used up within 24 hours after opened.
Product packing
- 25kg in each package, of which the grafted polyethylene (compound A) is 23.75 kg/bag, catalytic master batch material (compound B) is 1.25 kg/bag.
- Compound A and B are in moisture resistant aluminum laminated bags with composite paper bags outside.